NC-A high-rate and long cycle life aqueous electrolyte battery for grid-scale energy storage


ARTICLE
Received 22 May 2012 | Accepted 18 Sep 2012 | Published 23 Oct 2012
DOI: 10.1038/ncomms2139

A high-rate and long cycle life aqueous electrolyte battery for grid-scale energy storage
Mauro Pasta1,*, Colin D. Wessells1,*, Robert A. Huggins1 & Yi Cui1,2

New types of energy storage are needed in conjunction with the deployment of solar, wind and other volatile renewable energy sources and their integration with the electric grid. No existing energy storage technology can economically provide the power, cycle life and energy efficiency needed to respond to the costly short-term transients that arise from renewables and other aspects of grid operation. Here we demonstrate a new type of safe, fast, inexpensive, long-life aqueous electrolyte battery, which relies on the insertion of potassium ions into a copper hexacyanoferrate cathode and a novel activated carbon/polypyrrole hybrid anode. The cathode reacts rapidly with very little hysteresis. The hybrid anode uses an electrochemically active additive to tune its potential. This high-rate, high-efficiency cell has a 95% round-trip energy efficiency when cycled at a 5C rate, and a 79% energy efficiency at 50C. It also has zero-capacity loss after 1,000 deep-discharge cycles.

1 Department of Materials Science and Engineering, Stanford University, 476 Lomita Mall, McCullough 343, Stanford, California 94305, USA. 2 SLAC

National Accelerator Laboratory, Stanford Institute for Materials and Energy Sciences, 2575 Sand Hill Road, Menlo Park, California 94025, USA. *These authors equally contributed to this work. Correspondence and requests for materials should be addressed to Y.C. (email: yicui@stanford.edu).
nature communications | 3:1149 | DOI: 10.1038/ncomms2139 | www.nature.com/naturecommunications



? 2012 Macmillan Publishers Limited. All rights reserved.

ARTICLE

nature communications | DOI: 10.1038/ncomms2139

T

he increasing deployment of renewable energy sources such as solar and wind power requires a commensurate increase in energy storage capacity to integrate them into the electrical power grid1,2. Combining these sources with the energy grid is especially challenging because of the large, rapid variability in their output. Intermittent spikes or drops in power must be smoothed for durations as short as a few seconds, whereas load balancing is needed to counter diurnal fluctuations1,3. Inexpensive energy storage that has rapid response, long cycle life, high power and high energy efficiency that can be distributed throughout the grid is needed to allow broad penetration of solar, wind and other variable energy sources. Conventional energy storage technologies struggle to meet the needs of the grid2. Virtually, all of the energy storage capacity currently on the grid is provided by pumped hydroelectric power, which requires an immense capital investment, is location-dependent and suffers from low energy efficiency1,4. Compressed air energy storage is also site-dependent and must be supported by a fossil fuel-burning plant. Mechanical flywheels offer high power and efficiency, but they are far too expensive. Several battery technologies have seen limited deployment on the grid4,5. Lead acid cells are the least expensive, but have limited depth of discharge, cycle life and efficiency. Sodium–sulphur, sodium–metal halide and redox-flow batteries operate only at low rates and have low energy efficiencies. Finally, the lithium ion and nickel/metal hydride batteries used in electric vehicles are currently far too costly for use on larger scales. A variety of novel aqueous alkali-ion battery chemistries have been explored in recent years. They are potentially advantageous owing to the safety, high ionic conductivity and low cost of aqueous electrolytes. Aqueous lithium-ion batteries using cathode materials adopted from commercialized organic electrolyte cells have been explored, but in general they have shown limited cycle life6–8. Aqueous sodium cells using a NaxMnO2 cathode and a capacitive carbon anode have been demonstrated to offer long cycle life, but have limited rate capability9,10. These aqueous battery technologies have been limited primarily by the development of anode materials that have the correct potential and that are chemically stable at the desired electrolyte pH11. Recently, we developed a family of open-framework nanoparticle materials with the Prussian Blue crystal structure12–15. These materials have an open-framework crystal structure containing large interstitial sites that allows fast insertion and extraction of Na?+? and/or K?+? with very little crystallographic lattice strain. For example, copper hexacyanoferrate (CuHCF) reacts with K?+? by a single-phase insertion reaction:
2K x Cu y [Fe (CN)6 ] + a(K + e ) = 2K x + aCu y [FeIII (CN)6 ]1?a[FeII (CN)6 ]a
III + ?

at too high a potential (0.45?V versus SHE)18 and other Prussian Blue analogues containing electrochemically active hexacyanomanganate and hexacyanochromate are chemically unstable19. In this work, we describe a new class of anodes that are compatible with our open-framework CuHCF materials in aqueous electrolytes. These anodes are based on a hybrid electrode that operates by a new fundamental concept; that is, by combining an electrode material (polypyrrole, PPy), which is capable of a faradaic reaction at a fixed potential with a capacitive electrode (activated carbon, AC), the potential of the entire electrode can be controlled. Fundamentally different from traditional capacitive and battery electrodes, our new hybrid electrode has the high-rate capability of an ultra-capacitor, but with the well-defined potential of a battery electrode. This hybrid electrode has an attractive opencircuit potential (OCP), tunable to ???0.2?V versus SHE, a shallow charge/discharge profile and low self-discharge. Furthermore, we demonstrate that a full cell with this hybrid anode and a CuHCF cathode gives performance which is promising for grid-scale stationary storage applications, such as high power and energy efficiency, and a lifetime of thousands of cycles.

Results Hybrid-AC/PPy anode. Electrochemical double-layer capacitors (EDLCs) are known to operate in a variety of aqueous and organic electrolytes, and can have extremely high specific power and cycle life20. However, the cycling of an EDLC electrode proceeds by the physical formation and dispersal of a double layer of charge at the electrode surface with no faradaic reaction involving the bulk material21. This results in very low specific capacity and deleterious self-discharge2. Another drawback is that the potential of a capacitive electrode varies nearly linearly with charge state, so capacitors offer useful energy and power only at shallow discharge21. In addition, in the case of AC, negatively charged surface groups that improve hydrophilicity also raise the OCP in aqueous electrolytes to above 0.3?V versus SHE, which is too high for a useful anode with a CuHCF cathode22,23. One benefit of using AC as an anode in aqueous electrolytes is its suppression of H2 evolution at low potentials24, but its low capacity, steep discharge profile and high OCP limit its practicality. The electrochemical properties of conductive polymers such as PPy have been explored in both organic and aqueous electrolytes25,26. PPy is very insoluble in aqueous electrolytes26. Its electrochemical cycling proceeds by a p-type doping/de-doping process:
x+ (Py )n + yA ? ←?????? →(Py (x + y )+ yA ? )n + ye ? dopingdedoping

CuHCF electrodes are promising for grid-scale energy storage applications because of their ultra-long cycle life (83% capacity retention after 40,000 cycles), high power (67% capacity at 80C), high energy efficiency and, potentially, a very low cost. An anode to operate in the same electrolyte as the CuHCF cathode must be chemically stable in acidic solutions (pH 1–2)16 and preferably have a potential near ???0.1?V versus the standard hydrogen electrode (SHE), the thermodynamic limit for water decomposition at this pH. In addition, a useful anode must have a very long cycle life and high-rate capability to match the remarkable properties of the CuHCF cathode. In addition to K?+?, CuHCF can also react with alkali ions, such as Li?+? and Na?+?, so an anode capable of reacting with any of these ions could be used17. An intuitive choice would be another Prussian Blue analogue with a reaction potential near the SHE. However, the reduction of Prussian Blue to Everitt’s Salt occurs


Anions from the electrolyte coordinate to the PPy chains during oxidation, and they are released during reduction27. The reduction and oxidation of the polymer could also be balanced by smaller ions, such as H3O?+? in acidic aqueous electrolytes, which can fit into the existing paracrystalline lattice as previously demonstrated in the case of poly(3,4-ethylenedioxythiophene)28. The reaction potential of PPy depends on the particular doping anion29, but is typically near 0?V versus SHE, making it attractive for use as an anode in aqueous cells (Fig. 2a). A PPy anode was recently paired with LiCoO2 in an aqueous lithium-ion battery, but its low electronic conductivity upon reduction severely limited the rate capability, energy efficiency and cycle life of the cell27. Although it has a high theoretical specific capacity of 82?mAh?g???1 (ref. 30), PPy alone cannot be used as a high-performance anode. Here we combine an EDLC with PPy into a hybrid electrode synergistically. We explore using PPy as a minor additive component to define the potential of AC, whereas most of the charge storage is by AC. For this purpose, PPy nanoparticles (Fig. 1d,f) were

nature communications | 3:1149 | DOI: 10.1038/ncomms2139 | www.nature.com/naturecommunications

? 2012 Macmillan Publishers Limited. All rights reserved.

nature communications | DOI: 10.1038/ncomms2139

ARTICLE
– + = K+ = CuII = FeIII

a

= H2PO4– = PPy = AC

b

c

d

e

Intensity (a.u.)

PPy

CuHCF
5 10 15 20 25 30 35 40 45 50 55 60 65 70 75 80

2? (°)

f

Figure 1 | Full cell schematic and physical characterization of the electrode materials. (a) Schematic diagram of full cell device. In the PPy/AC negative electrode (b), the reduced PPy particles fix the open-circuit potential close to the lower-stability limit of the electrolyte, whereas the charge is stored in the electrical double layer at the high-surface AC. The CuHCF-positive electrode (c) has the open-framework Prussian Blue crystal structure, in which transition metal ions are linked by a face-centered cubic framework of cyanide groups. In the case of CuHCF, octahedral hexacyanoferrate groups form a framework with sixfold nitrogen-coordinated copper. The framework contains large interstices, known as the ‘A Sites’, which may contain zeolitic water or mobile, hydrated alkali ions. Hydrated ions may readily pass between one A Site and the next through channels in the ?<?100?>? directions. This three-dimensional network of A Sites and channels allows for rapid transport of K?+? through the material without disturbing the framework. Zeolitic water is omitted for clarity. (d) X-ray diffraction patterns of CuHCF and PPy. Bulk synthesis of CuHCF at room temperature by co-precipitation results in highly crystalline material. PPy particles are about 200–400?nm. At 2θ?=?11.5° and 26°, there are two broad peaks in the XRD pattern, indicating the existence of a short-range order and an ordered structure between the PPy chains. (e) Transmission electron microscope photo of CuHCF shows polydispersed 20–50?nm particles. Scale bar equals 100?nm. (f) Scanning electron microscope photo of PPy shows particles of the order of 200–400?nm. Scale bar equals 2??m.

synthesized by oxidative polymerization of pyrrole31. This hybrid anode combines the fast kinetics of AC and the low reaction potential of fully reduced PPy. In practice, this combination of properties can be achieved simply by intimately mixing AC with small amounts of reduced PPy in a single-electrode structure. This occurs because the OCP of AC and other EDLCs depends on its surface charge density and, therefore, is well-defined. Thus, in the case of electrical contact between AC and a material having a distinct redox couple, the OCP of the AC will be fixed to the potential of that redox couple. So, in the case of an AC/PPy electrode, the OCP is determined by the potential of the PPy component despite its small

quantity. The as-synthesized PPy powder is fully oxidized (doped) and has a high OCP of 0.5?V versus SHE. An electrode containing doped PPy and AC will also have a high OCP as explained above. Using a previously reported method for the reduction of pure PPy powder by sodium borohydride (NaBH4), electrodes containing both AC and PPy can be reduced, resulting in an OCP of ???0.1?V versus SHE (Fig. 2)32. Effect of the PPy/activated-carbon ratio. To look for the ideal PPy percentage that can define the OCP of ???0.1?V versus SHE while storing charge in the AC component, we have carried out experiments


nature communications | 3:1149 | DOI: 10.1038/ncomms2139 | www.nature.com/naturecommunications

? 2012 Macmillan Publishers Limited. All rights reserved.

ARTICLE
a
5.0 4.0 3.0 J mA–1 cm–2 2.0 1.0 0.0 –1.0 –2.0 –3.0 –4.0 –5.0 –0.4 –0.2 0.0 0.2 0.4 0.6 0.8 1.0 1.2 1.4 Potential versus SHE (V) CuHCF PPy

nature communications | DOI: 10.1038/ncomms2139

b
Potential versus SHE (V)

1.25 1.00 0.75 0.50 0.25 0.00 –0.25 –0.50 –10 0

Pure AC

CuHCF AC before NaBH4 reduction AC after NaBH4 reduction 10 20 30 40 50 Specific capacity (mAh g –1 ) CuHCF 25% PPy 60

c
Potential versus SHE (V)

1.25 1.00 0.75 0.50 0.25 0.00 –0.25 –0.50 0 10 20 30

10% PPy

d
Potential versus SHE (V)

1.25 1.00 0.75 0.50 0.25 0.00 –0.25 –0.50 0 10 20 30

NaBH4

NaBH4

40

50

60

40

50

60

Specific capacity (mAh g –1 ) CuHCF

Specific capacity (mAh g –1 ) CuHCF

e
Potential versus SHE (V)

1.25 1.00 0.75 0.50 0.25 0.00 –0.25 –0.50 0 10 20 30

50% PPy

f
Potential versus SHE (V)

1.25 1.00 0.75 0.50 0.25 0.00 –0.25 –0.50 0 10 20 30

100% PPy

40

50

60

40

50

60

Specific capacity (mAh g –1 ) CuHCF

Specific capacity (mAh g –1 ) CuHCF

Figure 2 | Hybrid AC/PPy anode. (a) Cyclic voltammetry scans of CuHCF and PPy at 1?mV?s???1 scan rate, (b–f) galvanostatic cycling of PPy/AC anodes at different ratios of PPy/AC at 1C rate. PPy/AC anodes before (---) and after (—) the NaBH4 chemical reduction step with 0.1?M NaBH4 and CuHCF cathode (···). The specific capacity values have been normalized by the mass of cathode, which is on the order of 10?mg?cm???2, whereas the anode mass is on the order of 50?mg?cm???2. The open-circuit potentials of the electrodes are on the right-end side for the cell cycling started from full discharge.

with five different PPy percentages: 0, 10, 25, 50 and 100%. We have found that hybrid AC/PPy electrodes have very interesting electrochemical properties, depending on the percentage of PPy. First, all the electrodes with or without PPy have high OCP of about 0.4?V versus SHE before the NaBH4 reduction treatment. These electrodes do not have an attractive voltage to pair with CuHCF. Second, after NaBH4 reduction treatment, all the electrodes containing PPy (Fig. 2c–f) have a significantly lower OCP of ???0.25?V versus SHE. This OCP is low enough for practical use with the CuHCF cathode. In comparison, pure AC electrodes do not undergo faradaic reactions, and their OCP is not lowered by NaBH4 chemical reduction (Fig. 2b). This difference is clearly due to the reduction of PPy by NaBH4, but the NaBH4 does not change the AC. Third, as the fractional PPy content of the hybrid electrode increases from 10 to 100%, the voltage hysteresis observed during cycling at a 1C rate grows dramatically (Fig. 2c–f). This occurs because fully reduced PPy is electronically


insulating33. Hybrid electrodes with a PPy content as low as 10% result in the same low, stable OCP of a pure PPy electrode. AC/PPy electrodes of even lower PPy content did not have stable OCPs (data not shown). The optimal PPy content was found to be 10%, as this quantity was sufficient to maintain a stable, low OCP and cycling potential without limiting the high efficiency of the AC. CuHCF chemical reduction. The novel AC/PPy hybrid anode can be combined with a wide variety of cathodes to produce full cell batteries. The hybrid anode with 10% PPy is used for the following full cell study. Here, we demonstrate its use in cells that contain CuHCF cathodes. When constructing a full cell with a CuHCF cathode and an AC/PPy hybrid anode, additional complications must be addressed. First, the two electrodes in a full cell must have appropriate initial charge states. The AC/PPy anode was chemically reduced so that its OCP was equal to the reaction potential of fully

nature communications | 3:1149 | DOI: 10.1038/ncomms2139 | www.nature.com/naturecommunications

? 2012 Macmillan Publishers Limited. All rights reserved.

nature communications | DOI: 10.1038/ncomms2139

ARTICLE
1.0 0.9 0.8

a

100 80

b
Cathode OCP versus SHE (V) Lattice parameter (?)

10.12 10.10 10.08 10.06 10.04 10.02

Charge state (%)

60 40 20 0

0.7 0.6 0.5 0.4 0.3 0.0 0.2 0.4 0.6 0.8 1.0 Molar ratio Na2S2O3 /CuHCF

0.0

0.2

0.4

0.6

0.8

1.0

Molar ratio Na2S2O3 /CuHCF
220

c
100%

d
200 111

400 420 422

Intensity (a.u.)

80% 60% 40% 20% 0%

Intensity (a.u.)

52

54 2? (°)

56

58

10

20

30

40 50 2? (°)

Figure 3 | CuHCF chemical reduction. (a) Charge state of the CuHCF and cathode open-circuit potential as a function of the molar ratio Na2S2O3 added/ CuHCF. The decrease in the lattice parameter of CuHCF with chemical reduction (b) is illustrated by the shift of the ?<?600?>? diffraction peak to smaller angles (c,d). The lattice parameters in d are the average calculated for ten diffraction peaks. The error bars are ?±?1 s.d. around this value.

reduced PPy. Previous syntheses of CuHCF resulted in a material with a fractional initial charge state, because fully oxidized CuHCF has a potential so high that it can be reduced by water. To address this concern, a reductive titration method was developed to controllably reduce CuHCF to a desired oxidation state and OCP using sodium thiosulfate (Na2S2O3; Fig. 3a). In the case of full reduction of CuHCF, this reaction may be described by:
2K x Cu y [FeIII (CN)6 ] + 2Na 2S2O3 + 2K + = 2K1+ x Cu y [FeII (CN)6 ]2 + Na 2S4O6 + 2Na +

Before the addition of any Na2S2O3, CuHCF is about 80% charged, so the addition of Na2S2O3 in a ratio of Na2S2O3:CuHCF of 0.8 results in full reduction. CuHCF can intercalate either K?+? or Na?+?. Though both K?+? and Na?+? are present during the reductive titration, CuHCF intercalates only K?+? because of its higher-equilibrium reaction potential14, and the OCPs observed after chemical reduction correspond to the potential of CuHCF observed at the same charge state during electrochemical cycling. Electrochemical reduction of CuHCF and other Prussian Blue analogues results in a decrease in lattice parameter, as the iron–carbon bond in Fe(CN)6 shortens by 0.05?? (Fig. 3b–d)34. Full cell assembly. Full cells were assembled with electrodes in their discharged states. Fully reduced CuHCF that was treated with Na2S2O3 in a 0.8:1 molar ratio was used as the cathode. The anode was 10% PPy/AC, pretreated with NaBH4. It is initially counterintuitive to consider a reduced anode to be in a discharged state; but as previously noted, the only role of the PPy additive is to fix the OCP of the electrode at the desired value; to have low hysteresis and therefore high energy efficiency, the contribution of the doping/

dedoping process of PPy to the electrode capacity must be negligible. For this reason, the anode was cycled over a potential range below that of the dedoping process of the PPy additive. In the first cycle, the battery is charged from its initial state, meaning that potassium ions are removed from the CuHCF framework at the cathode and that a charge double layer is formed at the anode. Another challenge for the development of a full cell using CuHCF and AC/PPy electrodes is the disparity in the specific capacities of the electrodes. The double-layer capacitance in aqueous electrolytes is 10–50??F?cm???2, so EDLCs must be cycled over wide potential ranges to achieve appreciable capacity21. Aqueous batteries have low voltages that are limited by water decomposition. A flat fullcell voltage profile is desirable because the stored energy scales with voltage, and the output power scales with the square of the voltage. If the voltage varies greatly with charge state, some of the charge is available only at voltages too low to provide practical values of energy and power. Therefore, electrodes in aqueous batteries should preferably be cycled over limited potential ranges so that the full discharge of the device produces usable energy. In the case of capacitive electrodes, the same charge can be accessed in a smaller potential window if a larger exposed surface and, therefore, a larger mass is used. The CuHCF versus AC/PPy cells described here contained a 10?mg?cm???2, 1?cm2 CuHCF cathode and a 50?mg?cm???2, 2?cm2 AC/ PPy anode, resulting in a cathode/anode mass loading ratio of 1:10. In full cells, the electrolyte must also be optimized to allow reversible cycling of both electrodes. Previous studies of CuHCF and other Prussian Blue analogues used electrolytes with pH between 2 and 416. In the full cells reported here, CuHCF was found to be most chemically stable at pH 1.

Discussion Full cell cycling with potential cut-off values of 0.85 and 1.1?V for the CuHCF cathode resulted in a full cell voltage range of 1.4–0.9?V


nature communications | 3:1149 | DOI: 10.1038/ncomms2139 | www.nature.com/naturecommunications

? 2012 Macmillan Publishers Limited. All rights reserved.

440 600 620 533 444 640 642

311

100% 80% 60% 40% 20% 0%

60

70

ARTICLE
a
Full cell voltage (V) 1.6 1.4 1.2 1.0 0.8 0.6 0.4 0.2 0.0 0
1C 10C 50C

nature communications | DOI: 10.1038/ncomms2139

b
Energy efficiency (%)

100 0.9 80 60 40 0.3 20 0
Energy efficiency Fractional capacity retention

Fractional capacity retention

0.6

10

20

30

40

50

60

0

10

20

30 C rate

40

50

0.0

Specific capacity (mAh g–1)

c
Potential versus SHE

1.50 1.25 1.00 0.75 0.50 0.25 0.00 –0.25 –0.50 0 10 20 30 40 50
(+) CuHCF (–) 100% PPy/AC Full cell profile

d
Specific capacity (mAh g–1 )

60 50 40 30 20 10 0 0 200 400 600 800

1.00 0.99 0.98 0.97 0.96 0.95 1,000

Coulombic efficiency

Specific capacity (mAh g–1)

Cycle number

Figure 4 | Full cell electrochemical characterization. (a) Full cell potential profiles at different C rates (1C, 10C, 50C). (b) Energy efficiency and fractional capacity retention as a function of the C rate. (c) Potential profiles of CuHCF-positive electrode, 10% PPy/AC anode-negative electrode and full cell profile at 10C. (d) Cycling of the CuHCF–10% PPy/AC cell at a rate of 10C showed no capacity loss after 1,000 cycles and a coulombic efficiency of 99.9%.

(Fig. 4a,c) and a maximum specific capacity of 54?mAh?g???1 CuHCF. Because of its high mass loading, the potential of the AC/PPy anode changes by only 250?mV during cycling, so the changes in the potentials of the two electrodes contribute similarly to the slope of the full cell voltage profile. The potential hysteresis of the anode is higher than that of the cathode because of its high mass loading (50?mg?cm???2) and thickness (1?mm). At a 10C rate, 82% of the maximum specific capacity is retained, with a round-trip energy efficiency of 92% (Fig. 4b), and at a rate of 50C 33% of the maximum specific capacity is observed at an efficiency of 79%. Cycling was highly reversible, with zero-capacity loss after 1,000 cycles at a 10 C rate, and the coulombic efficiency was 99.9% (Fig. 4d). The high capacity retention and rate capability of the CuHCF versus AC/PPy full cells result in high specific power. The average specific power during discharge at a 10C rate during cycling between 1.4 and 0.9?V was 45?W?kg???1 on the basis of the electrode active materials, and a maximum specific power of nearly 100?W?kg???1 was achieved at 20C. The specific energy of the cells reported here was about 5?W?h?kg???1, lower than the conventional lithium-ion, lead acid and NiMH batteries. However, as the discharge voltage was limited to 0.9?V, all of the specific energy of the cell can be practically used. The specific power and energy of the CuHCF versus AC/PPy cell is limited by the high mass loading of the anode. In this study, inexpensive, commercially available AC that was hydrophobic and, therefore, had a low effective surface area in water was used. Reducing the anode mass loading by 50% simply by using a more hydrophilic AC with a higher-effective specific surface area would nearly double the specific energy and power. Also, the cells reported here used a flooded geometry that resulted in excessive electrolyte resistance. The use of pressed cells will significantly improve energy efficiency and specific power at high cycling rates. In summary, novel aqueous potassium ion batteries using an open-framework crystal structure CuHCF cathode and a new type


of fixed-potential capacitive anode were demonstrated to have long cycle life, high power and high efficiency. The CuHCF cathode is synthesized by a simple, scalable, room-temperature chemical co-precipitation method. The anode combines commercially available, inexpensive AC with PPy, which may be synthesized in bulk near room temperature. The electrodes operate in safe, inexpensive aqueous electrolytes. The performance, scalability and safety of these cells make them desirable for stationary storage applications, including the smoothing of intermittent solar and wind power. The addition of electrochemically active additives with fixed potentials to capacitive electrodes may be employed in a wide variety of devices in which one or both of the electrodes is of this kind. Study of other types of devices using one or two EDLC/additive hybrid electrodes is underway.

Methods

CuHCF synthesis. Preparation of nanoparticulate CuHCF was based on our recently reported synthesis12. Briefly, equal volumes of 40?mM Cu(NO3)2 (Alfa Aesar) and 20?mM K3Fe(CN)6 (Sigma Aldrich) were combined by simultaneous, dropwise addition into water under vigorous stirring. An excess of Cu?+?2 is necessary for precipitation and particle growth. All of the Fe(CN)6 is oxidized initially, but fully charged CuHCF has a potential high enough to oxidize water. Thus, spontaneous partial reduction of CuHCF occurs, resulting in a fractional initial charge state, typically between 50 and 80% of total capacity. Five minutes after complete addition of the CuHCF precursors, 0.1?M Na2S2O3 was added until a desired molar ratio of FeIII(CN)6???3 to S2O3???2 was reached. The colour of CuHCF changed from a dingy yellow to deep claret upon addition of Na2S2O3, indicating a successful reduction. The CuHCF was filtered, washed with water and dried in vacuum at room temperature. Slurries containing CuHCF, amorphous carbon (Super P Li), poly(vinylidene) difluoride (Kynar HSV900) and graphite (Timcal KS6) in a ratio of 80:9:9:2 were prepared by grinding these materials by hand and then dispersing them in 1-methyl-2-pyrrolidinone. Electrodes with mass loadings of about 10?mg?cm???2 CuHCF were prepared by spreading the slurry on a carbon cloth current collector (Fuel Cell Earth). The electrodes were dried in vacuum at 60?°C for 1?h.

nature communications | 3:1149 | DOI: 10.1038/ncomms2139 | www.nature.com/naturecommunications

? 2012 Macmillan Publishers Limited. All rights reserved.

nature communications | DOI: 10.1038/ncomms2139
PPy synthesis. PPy was prepared by chemical oxidative polymerization of the corresponding monomer (pyrrole) in an aqueous medium as described elsewhere31. Pyrrole (0.03?mol, 2?ml) was dispersed in 150?ml of de-aerated (N2) cold water (0?°C). Anhydrous Na2S2O8 (oxidant; 6.61?g, 0.03?mol) was dissolved in 50?ml of cold (0?°C) water in a reaction vessel containing a magnetic stirring bar and added dropwise into the stirred pyrrole solution. The reaction was carried out for 8?h at 0?°C with moderate stirring. The precipitated PPy was filtered off, washed with distilled water and dried in vacuum at 60?°C for 8?h. The black PPy slurries containing 10% poly(vinylidene) difluoride and 90% active material, with AC and PPy in the desired ratio, were prepared in 1-methyl-2-pyrrolidinone. Negative electrodes with mass loadings of 50?mg?cm???2 were prepared by the method used for the CuHCF-positive electrodes. PPy chemical reduction. The chemical reduction of the PPy was carried out by immersing the electrodes for 20?min in a 0.1?M solution of NaBH4 as previously described in the paper by Bengoechea et al.32 The reduction process may also be performed on the raw PPy powder, but this could lead to material degradation if stored in air. Electrochemical cell set-up. Flooded full cells containing a CuHCF cathode, an AC/PPy anode, a 1?M potassium phosphate buffer at pH 1 and a Ag/AgCl reference electrode were prepared in a nitrogen-filled glovebox. The AC/PPy electrode is sensitive to oxidation, so the cell must be kept oxygen free to achieve efficient anode cycling at potentials below the SHE.

ARTICLE
17. McCargar, J. W. & Neff, V. D. Thermodynamics of mixed-valence intercalation reactions: the electrochemical reduction of Prussian blue. J. Phys. Chem. 92, 3598–3604 (1988). 18. Neff, V. D. Electrochemical oxidation and reduction of thin films of Prussian Blue. J. Electrochem. Soc. 125, 886–887 (1978). 19. Reguera, E., Bertrán, J. A. & Nu?ez, L. Study of the linkage isomerization process in hexacyanometallates. Polyhedron 13, 1619–1624 (1994). 20. Signorelli, R., Ku, D. C., Kassakian, J. G. & Schindall, J. E. Electrochemical double-layer capacitors using carbon nanotube electrode structures. Proc. IEEE 97, 1837–1847 (2009). 21. Conway, B. E. Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications (Kluwer Academic/Plenum, 1999). 22. Boehm, H. P. Some aspects of the surface chemistry of carbon blacks and other carbons. Carbon 32, 759–769 (1994). 23. Cheng, P. -Z. & Teng, H. Electrochemical responses from surface oxides present on HNO3-treated carbons. Carbon 41, 2057–2063 (2003). 24. Long, J. W et al. Asymmetric electrochemical capacitors–stretching the limits of aqueous electrolytes. MRS Bull. 36, 513–522 (2011). 25. Novák, P., Müller, K., Santhanam, K. S. V. & Haas, O. Electrochemically active polymers for rechargeable batteries. Chem. Rev. 97, 207–282 (1997). 26. Spila, E., Panero, S. & Scrosati, B. Solid-state ion battery. Electrochim. Acta 43, 1651–1653 (1998). 27. Wang, G. et al. An aqueous rechargeable lithium battery based on doping and intercalation mechanisms. J. Solid State Electrochem. 14, 865–869 (2010). 28. Aasmundtveit, K. E. et al. Structural aspects of electrochemical doping and dedoping of poly(3,4-ethylenedioxythiophene). Synth. Met. 113, 93–97 (2000). 29. Osaka, T., Naoi, K. & Ogano, S. Effect of polymerization anion on electrochemical properties of polypyrrole and on Li/LiClO4/polypyrrole battery performance. J. Electrochem. Soc. 135, 1071–1077 (1988). 30. Bittihn, R. et al. Polypyrrole as an electrode material for secondary lithium cells. Makromol. Chem. Macromol. Symp. 8, 51–59 (1987). 31. Blinova, N. V., Stejskal, J., Trchová, M., Proke?, J. & Omastová, M. Polyaniline and polypyrrole: a comparative study of the preparation. Eur. Pol. J. 43, 2331–2341 (2007). 32. Bengoechea, M. et al. Chemical reduction method for industrial application of undoped polypyrrole electrodes in lithium-ion batteries. J. Power Sources 160, 585–591 (2006). 33. Feldman, B. J., Burgmayer, P. & Murray, R. W. The potential dependence of electrical conductivity and chemical charge storage of poly(pyrrole) films on electrodes. J. Am. Chem. Soc. 107, 872–878 (1985). 34. Dostal, A., Kauschka, G., Reddy, S. J. & Scholz, F. Lattice contractions and expansions accompanying the electrochemical conversions of Prussian blue and the reversible and irreversible insertion of rubidium and thallium ions. J. Electroanal. Chem. 406, 155–163 (1996).

References

1. Rastler, D. Electricity energy storage technology options. EPRI Rep. 170 (2010). 2. Elkind, E., Abele, A. & Washom, B. 2020 Strategic Analysis of Energy Storage in California (2011). 3. Makarov, Y. V., Loutan, C., Jian, M. & de Mello, P. Operational impacts of wind generation on california power systems. Power Syst. IEEE Trans. 24, 1039–1050 (2009). 4. Yang, Z. et al. Electrochemical energy storage for green grid. Chem. Rev. 111, 3577–3613 (2011). 5. Soloveichik, G. L. Battery technologies for large-scale stationary energy storage. Ann. Rev. Chem. Biomol. Eng. 2, 503–527 (2011). 6. Li, W., Dahn, J. R. & Wainwright, D. S. Rechargeable lithium batteries with aqueous electrolytes. Science 264, 1115–1118 (1994). 7. Ruffo, R., Wessells, C., Huggins, R. A. & Cui, Y. Electrochemical behavior of LiCoO2 as aqueous lithium-ion battery electrodes. Electrochem. Commun. 11, 247–249 (2009). 8. Luo, J.- Y., Cui, W.- J., He, P. & Xia, Y. -Y. Raising the cycling stability of aqueous lithium-ion batteries by eliminating oxygen in the electrolyte. Nat. Chem. 2, 760–765 (2010). 9. Tevar, A. D. & Whitacre, J. F. Relating synthesis conditions and electrochemical performance for the sodium intercalation compound Na4Mn9O18 in aqueous electrolyte. J. Electrochem. Soc. 157, A870–A875 (2010). 10. Whitacre, J. F., Tevar, A. & Sharma, S. Na4Mn9O18 as a positive electrode material for an aqueous electrolyte sodium-ion energy storage device. Electrochem. Commun. 12, 463–466 (2010). 11. Manjunatha, H., Suresh, G. & Venkatesha, T. Electrode materials for aqueous rechargeable lithium batteries. J. Solid State Electrochem. 15, 431–445 (2011). 12. Wessells, C. D., Huggins, R. A. & Cui, Y. Copper hexacyanoferrate battery electrodes with long cycle life and high power. Nat. Commun. 2, 550 (2011). 13. Wessells, C. D., Peddada, S. V., Huggins, R. A. & Cui, Y. Nickel hexacyanoferrate nanoparticle electrodes for aqueous sodium and potassium ion batteries. Nano Lett. 11, 5421–5425 (2011). 14. Wessells, C. D., Peddada, S. V., McDowell, M. T., Huggins, R. A. & Cui, Y. The effect of insertion species on nanostructured open framework hexacyanoferrate battery electrodes. J. Electrochem. Soc. 159, A98–A103 (2012). 15. Wessells, C. D. et al. Tunable reaction potentials in open framework nanoparticle battery electrodes for grid-scale energy storage. ACS Nano 6, 1688–1694 (2012). 16. Stilwell, D. E., Park, K. H. & Miles, M. H. Electrochemical studies of the factors influencing the cycle stability of Prussian Blue films. J. Appl. Electrochem. 22, 325–331 (1992).

Acknowledgements

We thank Matt T. McDowell for transmission electron microscope characterization and Nian Liu for his help in drawing the full cell schematic. We also acknowledge support from the King Abdullah University of Science and Technology (KAUST) Investigator Award (no. KUS-l1-001-12).

Author contributions

M.P. and C.D.W. designed electrochemical and physical measurements. M.P. and C.D.W. performed and analysed electrochemical measurements and physical characterization. M.P., C.D.W., R.A.H. and Y.C. wrote this paper.

Additional information

Competing financial interests: The authors declare no competing financial interests. Reprints and permission information is available online at http://npg.nature.com/ reprintsandpermissions/ How to cite this article: Pasta, M. et al. A high-rate and long cycle life aqueous electrolyte battery for grid-scale energy storage. Nat. Commun. 3:1149 doi: 10.1038/ncomms2139 (2012).

nature communications | 3:1149 | DOI: 10.1038/ncomms2139 | www.nature.com/naturecommunications



? 2012 Macmillan Publishers Limited. All rights reserved.


相关文章:
A high-rate and long cycle life aqueous electrolyte battery ....unkown
Oct 2012 DOI: 10.1038/ncomms2139 A high-rate and long cycle life aqueous electrolyte battery for grid-scale energy storage Mauro Pasta1,*, Colin D....
...Hybrid Mg2 Li Battery with Long Cycle Life and High_图文_....pdf
Battery with Long Cycle Life and High Rate ...collectors by electrolyte components could have a ...Scale bar: 10 ?m. Inset in e): Pristine Pt...
...of High Rate, Long Cycle Life, Aqueous Electrolyte Batteries.unkown
a New Class of High Rate, Long Cycle Life, Aqueous Electrolyte Batteries...grid, requires the development of large-scale energy storage systems with a...
PHOTODEGRADATION OF ORGANIC POLLUTANTS INAQUEOUS SOLUTIONS ....unkown
INAQUEOUS SOLUTIONS CATALYZED BY IMMOBILIZEDTITANIUM ...a new laboratory-scale photocatalytic reactor for ...cycles resulted in higher absorption of UVA ...
High Rate, Long Cycle Life Aqueous Electrolyte Battery.unkown
High Rate, Long Cycle Life Aqueous Electrolyte Battery Mauro Pasta, Colin D...(CN)6]a CuHCF electrodes are promising for grid-scale energy storage...
New class of nonaqueous electrolytes for long life and safe ....unkown
New class of nonaqueous electrolytes for long life and safe lithium-ion ...(a) 2.0 1.5 Charge 1.0 Discharge 0.5 0.0 0 10 20 30 40 Cycle ...
A Review of Graphene-Based Electrochemical Microsupercapacitors.unkown
rechargeable micropower sources with high performance...scales in a modern technological society necessitate... with fast power delivery and long cycle life, ...
Heterogeneous nanostructured electrode materials for ....unkown
a different demand (e.g., high energy density,...A typical commercial lithiumion battery is ... (anode), a non-aqueous liquid electrolyte, ...
Large Scale Aqueous Electrolyte Sodium Ion Based Energy ....unkown
Scale Aqueous Electrolyte Sodium Ion Based Energy ...grid applications with bus voltages in the in ...Aquion Energy 30 Wh 1.3V nominal battery unit....
...in Li-S Batteries using Non-Aqueous Electrolytes: A High-....unkown
Supporting Information Towards a Molecular Understanding of Energetics in Li-S Batteries using Non-Aqueous Electrolytes: A High-level Quantum Chemical Study ...
http://energy.gov/sites/prod/files/FY05LDRDReport.pdf.unkown
Battery Anodes Multiphase CFD Analysis of Vascular Lesion Formation Science and...A New Low Temperature Thermochemical Hydrogen Production Cycle Based on Heavy ...
edbourret@lblgov.unkown
battery Growth of Nanoporous Palladium and Palladium...(3) a characteristic length scale develops from ...aqueous electrolyte, and with a flow cell, over...
...and good cycling performance in aqueous electrolyte.unkown
high rate capability and good cycling performance in aqueous electrolyte Zhi...most promising stationary power sources for large-scale energy storage devices...
...electrolyte for a high-energy density aqueous redox flow ....unkown
electrolyte for a high-energy density aqueous redox flow battery Bin Li1, ...scale the power and/or energya characteristic advantage along with high ...
...based assays for nucleoside and nucleotide metabolizing ....unkown
Development of capillary electrophoresis methods for high-resolution separation ...Development of a capillary electrophoresis method for the determination of ...
RECYCLING METALS FOR THE ENVIRONMENT.unkown
Opinions on long-term metals demand range from predictions that growth in ... and more efficient use in the economy will slow the rate of future ...
Ober¨chenphysik.unkown
in spite of the fact that the high band gap...a reduction of the tetracene/substrateinteraction,...nanometer scale is ofcrucial interest in many ...
SURFACE PLASMONIC CORE-SHELL PARTICLES FOR SOLAR ENERGY ....unkown
2014 Plasmonic core-shell particles, co
THE AQUEOUS ELECTROLYTE SODIUM ION BATTERY: A LOW-COST ....unkown
THE AQUEOUS ELECTROLYTE SODIUM ION BATTERY: A LOW...grids of the world grow and age, and as ...scale secondary (rechargeable) energy storage ...
...Intercalation Batteries with Aqueous Electrolytes.unkown
aqueous electrolyte based multivalent intercalation ...battery systems in aqueous electrolytes, and while...other large and small scale applications [18]...
更多相关标签: